ASTM A453 660A
Alias
ASTM A453
1.4980
X6NiCrTiMoVB 25 15 2
660
HR51
HR525
HR650
DTD 5076
A286
Chemistry
| Element | Min | Max |
|---|---|---|
| Al (Aluminium) | 0.35% | |
| B (Boron) | 0.001 | 0.01% |
| C (Carbon) | 0.08% | |
| Cr (Chromium) | 13.5 | 16% |
| Mn (Manganese) | 2% | |
| Mo (Molybdenum) | 1 | 1.5% |
| Ni (Nickel) | 24 | 27% |
| P (Phosphorus) | 0.04% | |
| S (Sulphur) | 0.03% | |
| Si (Silicon) | 1% | |
| Ti(Titanium) | 1.9 | 2.35% |
| V(Vanadium) | 0.1 | 0.5% |
| Mechanical Property | Min | Max |
|---|---|---|
| Ultimate Tensile Strength (UTS) | 895 MPa | |
| 0.2% Proof Stress | 585 MPa | |
| Elongation | 15% | |
| Gauge Length | A4D | |
| Hardness (Brinell) | 248 | 341HB |
| Hardness (Rockwell C) | 24 | 37 HRC |
Properties
Stress Rupture
High temperature Stainless Steel
Disclaimer:
Information is given for illustrative purposes only. Tachart accepts no responsibility for the accuracy of the data contained within or the use of the data by any other party.